Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Article
  • Published:

High-brightness all-polymer stretchable LED with charge-trapping dilution

This article has been updated

Abstract

Next-generation light-emitting displays on skin should be soft, stretchable and bright1,2,3,4,5,6,7. Previously reported stretchable light-emitting devices were mostly based on inorganic nanomaterials, such as light-emitting capacitors, quantum dots or perovskites6,7,8,9,10,11. They either require high operating voltage or have limited stretchability and brightness, resolution or robustness under strain. On the other hand, intrinsically stretchable polymer materials hold the promise of good strain tolerance12,13. However, realizing high brightness remains a grand challenge for intrinsically stretchable light-emitting diodes. Here we report a material design strategy and fabrication processes to achieve stretchable all-polymer-based light-emitting diodes with high brightness (about 7,450 candela per square metre), current efficiency (about 5.3 candela per ampere) and stretchability (about 100 per cent strain). We fabricate stretchable all-polymer light-emitting diodes coloured red, green and blue, achieving both on-skin wireless powering and real-time displaying of pulse signals. This work signifies a considerable advancement towards high-performance stretchable displays.

This is a preview of subscription content, access via your institution

Access options

Rent or buy this article

Prices vary by article type

from$1.95

to$39.95

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: Spontaneously formed nanofibre light-emitting structures of various colours for enhanced stretchability of light-emitting conjugated polymer films.
Fig. 2: Charge-trapping-dilution effect for enhancing electronic and optical performances of stretchable light-emitting conjugated polymer films.
Fig. 3: High-conductivity and highly stretchable PEDOT:PSS/PR electrode.
Fig. 4: Intrinsically stretchable, low-modulus and high-performance APLEDs and APLED arrays with different colours for wearable applications.

Similar content being viewed by others

Data availability

The data that support the findings of this study are available within this article and its Supplementary Information. Additional data are available from the corresponding authors on request. Source data are provided with this paper.

Change history

  • 06 April 2022

    In the version of this article initially published, bond lines were omitted in Fig. 3a, PEDOT and PSS structures; the bonds have now been restored

References

  1. Sekitani, T. et al. Stretchable active-matrix organic light-emitting diode display using printable elastic conductors. Nat. Mater. 8, 494–499 (2009).

    Article  CAS  PubMed  ADS  Google Scholar 

  2. Someya, T., Bao, Z. & Malliaras, G. G. The rise of plastic bioelectronics. Nature 540, 379–385 (2016).

    Article  CAS  PubMed  ADS  Google Scholar 

  3. Kim, J. H. & Park, J. W. Intrinsically stretchable organic light-emitting diodes. Sci. Adv. 7, eabd9715 (2021).

    Article  CAS  PubMed  PubMed Central  ADS  Google Scholar 

  4. Liang, J. et al. Elastomeric polymer light-emitting devices and displays. Nat. Photon. 7, 817–824 (2013).

    Article  CAS  ADS  Google Scholar 

  5. White, M. S. et al. Ultrathin, highly flexible and stretchable PLEDs. Nat. Photon. 7, 811–816 (2013).

    Article  CAS  ADS  Google Scholar 

  6. Larson, C. et al. Highly stretchable electroluminescent skin for optical signaling and tactile sensing. Science 351, 1071–1074 (2016).

    Article  CAS  PubMed  ADS  Google Scholar 

  7. Zhang, Z. et al. Textile display for electronic and brain-interfaced communications. Adv. Mater. 30, 1800323 (2018).

    Article  CAS  Google Scholar 

  8. Liang, J. et al. Silver nanowire percolation network soldered with graphene oxide at room temperature and its application for fully stretchable polymer light-emitting diodes. ACS Nano 8, 1590–1600 (2014).

    Article  CAS  PubMed  Google Scholar 

  9. Bade, S. G. R. et al. Stretchable light-emitting diodes with organometal-halide-perovskite-polymer composite emitters. Adv. Mater. 29, 1607053 (2017).

    Article  CAS  Google Scholar 

  10. Jiang, D. H. et al. Facile fabrication of stretchable touch-responsive perovskite light-emitting diodes using robust stretchable composite electrodes. ACS Appl. Mater. Interfaces 12, 14408–14415 (2020).

    Article  CAS  PubMed  Google Scholar 

  11. Li, Y. F. et al. Stretchable organometal-halide-perovskite quantum-dot light-emitting diodes. Adv. Mater. 31, 1807516 (2019).

    Article  CAS  Google Scholar 

  12. Xu, J. et al. Highly stretchable polymer semiconductor films through the nanoconfinement effect. Science 355, 59–64 (2017).

    Article  CAS  PubMed  ADS  Google Scholar 

  13. Zheng, Y. et al. Monolithic optical microlithography of high-density elastic circuits. Science 373, 88–94 (2021).

    Article  CAS  PubMed  ADS  Google Scholar 

  14. Chen, Y. et al. Flexible active-matrix electronic ink display. Nature 423, 136 (2003).

    Article  CAS  PubMed  ADS  Google Scholar 

  15. Zhang, Z. et al. A colour-tunable, weavable fibre-shaped polymer light-emitting electrochemical cell. Nat. Photon. 9, 233–238 (2015).

    Article  CAS  ADS  Google Scholar 

  16. Rein, M. et al. Diode fibres for fabric-based optical communications. Nature 560, 214–218 (2018).

    Article  CAS  PubMed  ADS  Google Scholar 

  17. Steude, A., Witts, E. C., Miles, G. B. & Gather, M. C. Arrays of microscopic organic LEDs for high-resolution optogenetics. Sci. Adv. 2, e1600061 (2016).

    Article  PubMed  PubMed Central  ADS  Google Scholar 

  18. Kim, D. et al. Ultraflexible organic light-emitting diodes for optogenetic nerve stimulation. Proc. Natl Acad. Sci. USA 117, 21138–21146 (2020).

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  19. Choi, S., Na, Y., Lee, J. & Choi, K. C. Textile-OLEDs with high wearing comfort used for fashion displays and phototherapy applications. Proc. Int. Conf. Display Technol. (ICDT) 52, 279 (2020).

    Google Scholar 

  20. Yu, H. et al. Direct acoustic imaging using a piezoelectric organic light-emitting diode. ACS Appl. Mater. Interfaces 12, 36409–36416 (2020).

    Article  CAS  PubMed  Google Scholar 

  21. Park, S. et al. Self-powered ultra-flexible electronics via nano-grating-patterned organic photovoltaics. Nature 561, 516–521 (2018).

    Article  CAS  PubMed  ADS  Google Scholar 

  22. Kim, D.-H. et al. Epidermal electronics. Science 333, 838–843 (2011).

    Article  CAS  PubMed  ADS  Google Scholar 

  23. Kim, Y. et al. A bioinspired flexible organic artificial afferent nerve. Science 360, 998–1003 (2018).

    Article  CAS  PubMed  ADS  Google Scholar 

  24. Yin, D. et al. Two-dimensional stretchable organic light-emitting devices with high efficiency. ACS Appl. Mater. Interfaces 8, 31166–31171 (2016).

    Article  CAS  PubMed  Google Scholar 

  25. Park, S. I. et al. Printed assemblies of inorganic light-emitting diodes for deformable and semitransparent displays. Science 325, 977–981 (2009).

    Article  CAS  PubMed  ADS  Google Scholar 

  26. Kee, S. et al. Highly deformable and see-through polymer light-emitting diodes with all-conducting-polymer electrodes. Adv. Mater. 30, 1703437 (2018).

    Article  CAS  Google Scholar 

  27. Park, J. et al. Highly customizable all solution-processed polymer light emitting diodes with inkjet printed Ag and transfer printed conductive polymer electrodes. Adv. Funct. Mater. 29, 1902412 (2019).

    Article  CAS  Google Scholar 

  28. Abbaszadeh, D. et al. Elimination of charge carrier trapping in diluted semiconductors. Nat. Mater. 15, 628–633 (2016).

    Article  CAS  PubMed  ADS  Google Scholar 

  29. Abbaszadeh, D. & Blom, P. W. Efficient blue polymer light-emitting diodes with electron-dominated transport due to trap dilution. Adv. Electron. Mater. 2, 1500406 (2016).

    Article  CAS  Google Scholar 

  30. Choong, C. L. et al. Highly stretchable resistive pressure sensors using a conductive elastomeric composite on a micropyramid array. Adv. Mater. 26, 3451–3458 (2014).

    Article  CAS  PubMed  Google Scholar 

  31. Kim, Y. H. et al. Highly conductive PEDOT:PSS electrode with optimized solvent and thermal post-treatment for ITO-free organic solar cells. Adv. Funct. Mater. 21, 1076–1081 (2011).

    Article  CAS  Google Scholar 

  32. Vosgueritchian, M., Lipomi, D. J. & Bao, Z. Highly conductive and transparent PEDOT:PSS films with a fluorosurfactant for stretchable and flexible transparent electrodes. Adv. Funct. Mater. 22, 421–428 (2012).

    Article  CAS  Google Scholar 

  33. Jiang, Y. et al. Topological supramolecular network enabled highly conductive and stretchable organic bioelectronics. Preprint at https://doi.org/10.1101/2022.01.16.476423 (2022).

  34. Mengistie, D. A., Wang, P. C. & Chu, C. W. Effect of molecular weight of additives on the conductivity of PEDOT:PSS and efficiency for ITO-free organic solar cells. J. Mater. Chem. A 1, 9907–9915 (2013).

    Article  CAS  Google Scholar 

  35. Bolink, H. J., Coronado, E., Orozco, J. & Sessolo, M. Efficient polymer light-emitting diode using air-stable metal oxides as electrodes. Adv. Mater. 21, 79–82 (2009).

    Article  CAS  Google Scholar 

  36. Fong, H. H., Papadimitratos, A. & Malliaras, G. G. Nondispersive hole transport in a polyfluorene copolymer with a mobility of 0.01 cm2 V−1 s−1. Appl. Phys. Lett. 89, 172116 (2006).

    Article  ADS  CAS  Google Scholar 

  37. Ohisa, S. et al. Conjugated polyelectrolyte blend with polyethyleneimine ethoxylated for thickness-insensitive electron injection layers in organic light-emitting devices. ACS Appl. Mater. Interfaces 10, 17318–17326 (2018).

    Article  CAS  PubMed  Google Scholar 

  38. Zhou, Y. et al. A universal method to produce low-work function electrodes for organic electronics. Science 336, 327–332 (2012).

    Article  CAS  PubMed  ADS  Google Scholar 

  39. Gann, E. et al. Soft x-ray scattering facility at the Advanced Light Source with real-time data processing and analysis. Rev. Sci. Instrum. 83, 045110 (2012).

    Article  CAS  PubMed  ADS  Google Scholar 

  40. Collins, B. A. et al. Polarized X-ray scattering reveals non-crystalline orientational ordering in organic films. Nat. Mater. 11, 536–543 (2012).

    Article  CAS  PubMed  ADS  Google Scholar 

  41. De Pauli, M. et al. Understanding molecular interactions in light-emitting polymer bilayers: the role of solvents and molecular structure on the interface quality. Appl. Phys. Lett. 104, 163301 (2014).

    Article  ADS  CAS  Google Scholar 

  42. Urquhart, S. G. et al. Near-edge X-ray absorption fine structure spectroscopy of MDI and TDI polyurethane polymers. J. Phys. Chem. B 103, 4603–4610 (1999).

    Article  CAS  Google Scholar 

Download references

Acknowledgements

Part of this work was performed at the Stanford Nano Shared Facilities (SNSF), supported by the National Science Foundation under award ECCS-1542152. We thank Agfa-Gevaert N.V. for providing PEDOT:PSS, Daikin Co. for providing PVDF-HFP and Kaneka Co. for providing SIBS. Y.-X.W. was supported by a visiting scholar funding (201806255002) from the China Scholarship Council. N.M. was supported by a Japan Society for the Promotion of Science (JSPS) Overseas Research Fellowship. This research used resources of the Advanced Light Source, a U.S. Department of Energy Office of Science User Facility under contract no. DE-AC02-05CH11231.

Author information

Authors and Affiliations

Authors

Contributions

Z.Z. and Z.B. conceived the idea. Z.B. directed the project. Z.Z., W.W., Y.J. and Y.-X.W. participated in materials synthesis, device fabrication and data processing. Z.Z. and W.W. developed stretchable light-emitting materials. Z.Z., Y.J. and Y.-X.W. developed the stretchable PEDOT:PSS electrode. Y.J. performed part of the AFM, UV and PL measurements. Y.Wu performed the PLQE, lifetime and energy-level measurements. Z.Z. and J.-C.L. performed the transmittance and device modulus tests and data collections. S.N. developed the flexible wireless power supply circuit. C.X. developed the system for testing real-time pulse signals. Z.Z. and C.-C.S. developed stretchable interlayers. C.W. and H.Y. performed the R-SoXS tests. L.G. and N.P. performed the thin-film mechanics tests and part of the AFM and modulus measurements. H.-C.W. performed the GIXD tests. D.Z. helped to collect part of the optical images of the stretchable PEDOT:PSS/PR electrode. G.C. performed the XPS measurements. N.M. helped with the discussion of stretchable interlayers. Y.Z. and Z.Y. performed the dichroic ratio tests. Y.Wang performed the part of modulus measurements. Z.Z., W.W., Y.J. J.B.-H.T. and Z.B. wrote and revised the paper.

Corresponding author

Correspondence to Zhenan Bao.

Ethics declarations

Competing interests

 Stanford University has filed a patent application related to this work, the patent application number is 63/314,875.

Peer review

Peer review information

Nature thanks Caroline Murawski and the other, anonymous, reviewer for their contribution to the peer review of this work.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Extended data figures and tables

Extended Data Fig. 1 AFM phase images of SY/PU films with increased PU amount.

The films were prepared by spin coating from a mixture solution of SY (7 mg ml−1) and PU (7 mg ml−1) in THF with different weight ratios and dried under vacuum (200 mTorr) for 30 min. Distinct nanofibre structures can be seen with the addition of PU.

Extended Data Fig. 2 Optical images of SY/PU films with increased PU amount at different strains.

The scale bar is 100 μm.

Extended Data Fig. 3 Photographs of stretchable light-emitting films with different colours for various wearable applications.

a, Photographs of photoluminescent images of a stretchable and patterned light-emitting polymer film under stretching and twisting. The scale bar is 5 mm. b, Photographs of photoluminescent images of a patterned light-emitting polymer film seamlessly integrated with the finger withstanding various deformations.

Extended Data Fig. 4

Spectrum of emission/absorption ratio of SY/PU films (nearly the same thickness) with increased amount of PU: collected from spin-coated films (a) and after normalization on the basis of SY unit mass (b).

Source data

Extended Data Fig. 5 2D contour plots of time-resolved PL of SY/PU films with increased PU amount while the film thicknesses were kept nearly the same.

A higher amount of PU resulted in longer lifetime, with the lifetime increasing from 1.49, 1.71, 1.72, 1.74, 1.84 to 1.85 ns.

Extended Data Fig. 6 Electron and hole current density versus driven voltage characteristics of SY/PU films with increased PU amount while the film thicknesses were kept nearly the same.

a, Electron current density–voltage curves. The trap-limited electron transport of SY/PU films with electron-only devices (ITO/Al/SY:PU/PFN-Br:PEIE/Al). The electron current densities were 0.0008, 0.0085, 0.0119, 0.0180, 0.0476 and 0.1383 A m−2, with PU amounts of 0, 30, 40, 50, 60 and 70 wt%, respectively. b, Hole current density–voltage curves. The trap-free hole transport of SY/PU films in a set of ITO/PEDOT:PSS:Triton X/SY:PU/MoO3/Au hole-only devices. The hole current densities were 52.7, 81.0, 255.4, 532.2, 327.1 and 350.7 A m−2 when increasing the PU amount.

Source data

Extended Data Fig. 7 PLED characteristics of SY/PU films on rigid ITO glass substrates with increased PU amount while the film thicknesses were kept nearly the same with the set of ITO/PEDOT:PSS:Triton X (8 nm)/TFB (40 nm)/SY:PU (120 nm)/PFN-Br:PEIE (10 nm)/Al (60 nm).

a, Current density–voltage curves. b, Luminance–voltage curves. c, Current efficiency–voltage curves. The luminance values were 10,868, 34,743, 19,227, 15,631, 11,159 and 2,365 cd m−2 with increased PU amount, whereas the current efficiencies were 4.1, 14.2, 13.1, 13.5, 13.5 and 13.3 cd A−1.

Source data

Extended Data Fig. 8 Energy level and optical bandgap for all the layers in APLEDs.

PESA measurements of SY/PU film (a), red polymer/PU film (b), green polymer/PU film (c), blue polymer/PU film (d), PFN-Br/PEIE film (e), TFB/PU film (f), PEDOT:PSS/Triton X film (g) and PEDOT:PSS/PR film (h). UV–vis absorption spectra of SY/PU film (i), red polymer/PU film (j), green polymer/PU film (k), blue polymer/PU film (l), PFN-Br/PEIE film (m) and TFB/PU film (n). Optical bandgap was estimated from the absorption edge of as-cast thin film. HOMO energies were determined by UV PESA. LUMO energies were calculated according to ELUMO = Eg + EHOMO.

Source data

Extended Data Fig. 9

Fabrication process of an intrinsically stretchable APLED.

Extended Data Fig. 10

Energy-level alignment diagrams, current density and luminance, and current efficiency–luminance curves of intrinsically stretchable APLEDs (PVDF-HFP/PEDOT:PSS:PR/PEDOT:PSS:Triton X/TFB:PU/RGB-coloured light-emitting polymers:PU/PFN-Br:PEIE/PEDOT:PSS:PR/PVDF-HFP) with red (ac), green (df) and blue (gi) colours.

Source data

Supplementary information

Supplementary Information

This file contains Supplementary Notes, Supplementary Figs. 1–30, Supplementary Tables 1–3, captions for Supplementary Videos 1–5 and Supplementary References.

Supplementary Video 1

A stretchable and multicolour light-emitting polymer film seamlessly integrated with the finger, withstanding various deformations.

Supplementary Video 2

A stretchable and multicolour light-emitting polymer film under stretching.

Supplementary Video 3

A stretchable and multicolour light-emitting polymer film under twisting.

Supplementary Video 4

A stretchable APLED seamlessly integrated with the skin under wireless powering at 9 V.

Supplementary Video 5

A stretchable APLED integrated with the skin showing real-time pulse signals.

Source data

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Zhang, Z., Wang, W., Jiang, Y. et al. High-brightness all-polymer stretchable LED with charge-trapping dilution. Nature 603, 624–630 (2022). https://doi.org/10.1038/s41586-022-04400-1

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1038/s41586-022-04400-1

This article is cited by

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing